Haynes® Waspaloy Alloy is an age-hardenable, nickel-based superalloy that possesses excellent strength at elevated temperatures.
Composition | UNS N07001 % |
Nickel | 58 balance |
Cobalt | 13.50 |
Chromium | 19 |
Molybdenum | 4.30 |
Iron | 2 max |
Aluminum | 1.5 |
Titanium | 3 |
Carbon | 0.08 |
Manganese | 0.01 max |
Silicon | 0.15 max |
Boron | 0.01 |
Metric | English | |
Density* | 8.20 g/cm³ | 0.296 lbs/in³ |
Modulus of elasticity* | 213 GPa | 30.9 x 10? psi |
Thermal conductivity* | 12.6 W/m °C | 88 Btu-in/ft²hr-°F |
*Density and modulus of elasticity at room temperature, thermal conductivity at 200° C [400° F].
Cold worked % | Yield strength | Ultimate tensile strength | Elongation % |
0 | 586 MPa [85 ksi] | 1027 MPa [149 ksi] | 43 |
20 | 1089 MPa [158 ksi] | 1262 MPa [183 ksi] | 11 |
37 | 1434 MPa [208 ksi] | 1731 MPa [251 ksi] | 3 |
All data represent results from a 25.4 cm [10 in] test gauge length. Values are typical and may not represent all diameters. Test method will affect results.