Similar to MP35N®, 35N LT® utilizes enhanced melt practices for ASTM F562 of which results in an improved fatigue life of as-drawn wire by as much as 800%.
ASTM F562 | |
Carbon | 0.025 |
Manganese | 0.15 |
Silicon | 0.15 |
Phosphorus | 0.015 |
Sulfur | 0.01 |
Chromium | 19-21 |
Nickel | 33-37 |
Molybdenum | 9-10.50 |
Cobalt | Balance |
Titanium | 0.01 |
Iron | 1 |
Boron | 0.015 |
English | Metric | |
Density | 0.304 lbs/in | 8.41 g/cm³ |
Modulus Of Elasticity | 33.8x106psi | 233 Gpa |
Electrical Resistivity | 40.7µohm-in | 1033 µohm-mm |
Thermal Conductivity | 77.7 Btu-in/hr-ft2°F | 11.2 W/mK |
Thermal Coefficient of Expansion | 7.11 µin/in-°F | 12.8 µm/m-°C |
For more detailed specifications on 35N LT® please click here.